EPGC308 Epoxy glass cloth laminated sheet

EPGC308 Epoxy glass cloth laminated sheet
Product Detailed
EPGC308 sheet has good dielectric properties and stable performance under high temperature.

1.EPGC308 Epoxy glass cloth laminated sheet.

2.EPGC308 sheet is made of alkali-free E-glass cloth impregnated with epoxy resins by processing under heat and pressure. 3.EPGC308 sheet of Temperature Index is 180°C,Mechanical,electrical and electronic applications.EPGC308 sheet has extremely high mechanical strength at moderate temperature.very good stability of electrical properties in high humidity,high mechanical strength at elevated temperature,but with improved thermal endurance properties.

4.EPGC308 sheet is mainly used in mechanical, electrical, electronics and other fields. 

5. EPGC308 sheet of The area:1020x1220mm (40"x48");1020x2040mm (40"x80")

Thickness:0.2-100mm (0.0079"-3.94")

Item

Unit

Value

Density

g/cm3

1.701.90

Flexural strength perpendicular to lamination  ≥

MPa

340

Charpy Impact strength parallel to laminations  ≥

kJ/m2

33

lzod impact strength parallel to laminations  ≥

kJ/m2

35

Voltage endurance perpendicular to lamination in transformer oil

at 90±2°C  ≥

  Thickness 0.5mm  Thickness 1.0mm  Thickness 2.0mm  Thickness 3.0mm

kV/mm

 

 

16.114.211.810.2

Voltage endurance parallel to lamination in transformer oil at 90±2°C ≥

kV

35

Insulation resistance after impregnated in water ≥

5×104

Thermal endurance ≥

TI

180

Water absorption  ≤

  Thickness 0.5mm  Thickness 1.0mm  Thickness 2.0mm  Thickness 3.0mm

 

mg

 

17182022

EPGC308 Epoxy glass cloth laminated sheet